CVD coated grade for milling cast iron F5020

F5020 is a general purpose milling grade for cast iron with greatly improved wear and fracture resistance as a result of Mitsubishi's proprietary, micro-structure controlling technology.

Improved wear resistance

Combining super fine grain, carbonize titanium layer and flat-alumna (Al2O3) layer, the F5020 coating has enhanced wear resistance over conventional products.

Improved fracture resistance

Due to the newly developed cemented carbide substrate for milling castiron, F5020 has improved thermal crack resistance. This allows for increased reliability and resistance to abrupt tool breakage from cutting edge chipping.

Preventing Built-Up edge

Surface coating layers are a lamination of special titanium compounds that is vapor deposited by Even Coating technology. This process prevents occurrences of welding, which is a cause of chipping on top cutting edge.

F5020 has the ability to cover a wide range of milling applications of cast iron.

Workpiece		Brinell hardness	Cutting speed (ft/min)	Feed per tooth (inch/tooth)
K	General cast iron	180 - 380 HB	660 (490 - 820)	0.008 (0.039 - 0.012)
	Ductile cast iron	180 - 300 HB	660 (490 - 820)	0.008 (0.039 - 0.012)
		200 - 300 HB	490 (320 - 660)	0.008 (0.039 - 0.012)